Catalyst for ammonia synthesis and ammonia decomposition

ABSTRACT

The present invention relates to a catalyst for ammonia synthesis and ammonia decomposition. The catalyst includes a nitrogen-containing compound of a main group element and a related support and an additive. The present invention is a novel catalytic material, which exhibits good catalytic activity in ammonia synthesis and ammonia decomposition reactions.

TECHNICAL FIELD

The present invention relates to a catalyst technology, and particularly provides a catalyst for ammonia synthesis and ammonia decomposition and applications thereof in ammonia synthesis and ammonia decomposition reactions.

BACKGROUND

Ammonia is a basic raw material for producing such important chemical products as fertilizers, nitric acid, plastics, etc., and at the same time is a hydrogen source carrier with a potential application prospect; thus the ammonia synthesis and decomposition have a very important significance in industry. The direct catalytic conversion of N₂ and H₂ is a main means of industrial ammonia synthesis. Because the reaction condition of the ammonia synthesis is harsh and the requirement for a device is very high, the energy consumption is very high, and the annually consumed energy is 1% of the total annual energy consumption in the world. Recently, the catalysts widely used for ammonia synthesis and ammonia decomposition in industry are respectively transition metal catalysts such as Fe-based catalyst, Ru-based catalyst, Ni-based catalyst, etc. However, for decades, the efficiency of ammonia synthesis has not been improved and increased significantly, and the reaction condition still needs high temperature and high pressure. For an ammonia decomposition reaction, the low-cost Ni-based catalyst, however, shows low activity. Therefore, the development of a novel ammonia synthesis and ammonia decomposition catalyst system with low-temperature, low-pressure activity and high-efficiency is a very important research topic at present. Without the limitations of the Fe and Ru-based catalyst, the research and development of catalysts of other components by referring to an existing basic theory and technology is an effective strategy of developing a new generation of ammonia synthesis and ammonia decomposition catalyst.

As for a non-Fe(Ru)-based catalyst of ammonia synthesis and decomposition, some progress has been made in recent years. Aika and Jacobsen et al. respectively reported that a transition metal nitride alloy shows good catalytic activity in ammonia synthesis. Under lower temperature and pressure, the activity of a Cs-promoted Co₃Mo₃N catalyst is superior to that of an industrially widely used multiply-promoted fused iron catalyst, and under certain condition, even is superior to that of the Ru-based catalyst [R. Kojima, K. Aika, Chem. Lett., 2000, 514-515; C. J. H. Jacobsen, Chem. Commu., 2000, 1057-1058.]. C. Li et al. used the transition metal nitride alloy supported on aluminium oxide in the ammonia decomposition reaction, and also obtained better catalytic activity [C. H. Liang, W. Z. Li, Z. B. Wei, Q. Xin, C. Li, Ind. Eng. Chem. Res., 2000, 39: 3694-3697.].

Ohtsuka et al. used calcium oxide supported on carbon-based materials in the decomposition reaction of ammonia of a low concentration (2000 ppm), and found that the catalyst shows certain catalytic ammonia decomposition activity above the temperature of 700° C. [Y. Ohtsuka, C. Xu, D. Kong, N. Tsubouchi, Fuel, 2004, 83: 685-692.].

In conclusion, the non-Fe(Ru)-based ammonia synthesis and ammonia decomposition catalyst has made some progress, but also is unable to achieve industrialization. Further study shall be made on how to regulate the catalyst composition and structure to enhance the activity and stability of the catalyst and reduce catalyst cost.

SUMMARY

NH₃ can be produced upon heating an alkali metal amide in a stream of hydrogen, and a reaction formula is as follows:

LiNH₂+H₂=LiH+NH₃

however, in such a process, LiNH₂ is a reactant rather than a catalyst. In 2002, the inventor reported that Li₂NH and Li₃N could conduct a reversible hydrogen absorption-desorption reaction at moderate temperatures, and hydrogenated products are LiNH₂ and LiH. Further experimental results showed that the LiNH₂ can be decomposed to emit NH₃ in the temperature range of 200 to 500° C. with the peak temperature at about 370° C. An interesting finding is that when the reaction temperature is higher than 400° C., a small amount of N₂ and H₂ are detected in the gaseous product, as shown in FIG. 1. Because the conversion rate of gaseous self-decomposition of NH₃ is very low at temperatures lower than 500° C., it is likely that LiNH₂ or Li₂NH can exhibit catalytic effect in the further decomposition of ammonia of the gaseous product.

To demonstrate this effect, we firstly adopt a method of temperature programming reaction to investigate the behavior of Li₂NH in a diluted ammonia (5% NH₃/Ar). As shown in FIGS. 2, N₂ and H₂ are produced at a temperature of 450° C. and gradually enhanced as the temperature increases, which evidence that the decomposition reaction of ammonia occurs in such a process. XRD results of the reacted sample show that the sample is still Li₂NH, which further confirms that Li₂NH has the catalytic effect in the ammonia decomposition.

The further study shows that nitrogen or/hydrogen-containing compounds of main group elements such as Na, K, Cs, Be, Mg, Ca, Sr, Ba, Al, etc. also have the similar catalytic activities. The nitrogen or/and hydrogen-containing compounds include mono-component or multi-component nitride, amide, imino compound, nitrogen oxide, nitride-hydride and hydride or a mixture of two or more, etc. The basic composition thereof is M_(x)N_(y)H_(m(3y-nx)), where M is one or more than two of an IA, IIA, IIIA group element, n (can be 1, 2 and 3) is the valence of M, and m (can be 1 and −1) is the valence of H; when m=1, the formula is M_(x)N_(y)H_(3y-nx), x=1-3, y=1-3; and when m=−1, the formula is M_(x)N_(y)H_(nx-3y), x=1-4, y=0-1.

The nitrogen or/and hydrogen-containing compounds of main group elements can be loaded on certain supports. The supports can be one of Li₂O, Na₂O, K₂O, MgO, CaO, SrO, BaO, SiO₂, Al₂O₃, BN, Si₃N₄, Mg₃N₂, Ca₃N₂, AlN, molecular sieve, carbon material and Metal-Organic Frameworks(MOF) or a combination of more than two. The mass ratio of the catalyst to the carrier is in a preferred range from 200:1 to 1:100.

Metal nitrides can be added to the nitrogen or/and hydrogen-containing compounds of the main group elements. The metal nitrides are IVB, VB, VIB, VIIB or VIIIB elements, such as one or more than two of nitrides of Ti, Zr, V, Nb, Ta, Cr, Mo, W, Mn, Fe,Co, etc. The mass ratio of the catalyst to the metal nitride is in the preferred range from 200:1 to 1:100.

Metal alloys can be added to the nitrogen or/and hydrogen-containing compounds of the main group elements. The metal alloys are IVB, VB, VIB, VIIB or VIIIB elements, such as alloy higher than binary or ternary alloy formed by synthesis of two or three of Ti, Zr, Cr, Mo, W, Mn, Fe, Ru, Co, Rh, Ir, Ni, Pd and Pt, or the IVB, VB, VIB, VIIB or VIIIB elements, such as alloy higher than binary or ternary alloy formed by one or more than two of Ti, Zr, Cr, Mo, W, Mn, Fe, Ru, Co, Rh, Ir, Ni, Pd and Pt and C and/or B. The mass ratio of the catalyst to the metal alloy is in the preferred range from 200:1 to 1:100.

In the ammonia decomposition reaction, by adopting the catalyst provided in the present invention, the relatively ideal effect can be obtained: a Fe₂N/LiNH₂ (molar ratio is 0.5:3) catalyst exhibits approximate activity compared with a 5 wt% Ru/CNTs catalyst prepared by a conventional impregnation method. In the ammonia synthesis reaction, the ammonia synthesis reaction rate of LiH in N₂/H₂ mixture (N₂:H₂=1:3) can reach 95 umol g_(cat) ⁻¹ h⁻¹ under reaction condition of 400° C. at constant pressure.

DESCRIPTION OF THE DRAWINGS

FIG. 1 shows the temperature programmed desorption of LiNH₂ (Ar-TPD).

FIG. 2 shows the temperature programmed reaction of Li₂NH in 5% NH₃/Ar (NH₃-TPR).

FIG. 3 shows the activities of Li₂NH, KNH₂ and Fe₂N in the 5% NH₃/Ar.

FIG. 4 shows the reaction activities of Fe₂N/LiNH₂ (molar ratio is 0.5:2) and Fe₂N/KNH₂ (molar ratio is 0.5:2) in the 5% NH₃/Ar.

FIG. 5 shows the reaction activities of Fe₂N/LiNH₂ (molar ratio is 0.5:3) and Fe₂N/KNH₂ (molar ratio is 0.5:2) in pure ammonia.

DETAILED DESCRIPTION

To further describe the present invention, the following specific embodiments are listed, but do not limit the invention scope defined by all appended claims.

EMBODIMENT 1

In an argon glovebox, Li₂NH of 0.0300 g is accurately taken in a fixed bed stainless steel reactor. The sample is heated to 400° C. in argon atmosphere, and the argon flow rate is 30 mL/min. After 20 min, 5% NH₃/Ar mixture is introduced, the reactant flow rate is controlled between 1.8 L/h and 3.6 L/h, and after 30 min, the sampling analysis is conducted. The measurement results are shown in FIG. 3. The NH₃ conversion rate increases approximately linearly as the temperature increases, and the NH₃ conversion rate can reach 35% at 450° C.

EMBODIMENT 2

In the argon glovebox, KNH₂ of 0.0300 g is accurately taken in the fixed bed stainless steel reactor. The sample is heated to 400° C. in argon atmosphere, after 20 min, 5% NH₃/Ar mixture is introduced, the reactant flow rate is controlled between 1.8 L/h and 3.6 L/h, and after 30 min, the sampling analysis is conducted. The measurement results are shown in FIG. 3. The ammonia conversion rate increases approximately linearly as the temperature increases. At the same reaction temperature, the activity thereof is a little more than that of the Li₂NH, and the NH₃ conversion rate can reach 35% at 440° C.

EMBODIMENT 3

In the argon glovebox, Fe₂N of 1.0000 g and LiNH₂ of 0.7300 g are accurately taken in a homemade stainless steel ball mill tank. After the ball mill tank is sealed, the sample Fe₂N/LiNH₂ (molar ratio is 0.5:2) is prepared by ball-milling Fe₂N and LiNH₂ under ball mill condition of 200 rpm in a planetary ball mill (Fischt PM400) for 5 h.

In the argon glovebox, Fe₂N/LiNH₂ (molar ratio is 0.5:2) of 0.0350 g is accurately taken in the fixed bed stainless steel reactor. The sample is heated to a desired temperature in reaction atmosphere (5% NH₃/Ar mixture), the reactant flow rate is controlled between 1.8 L/h and 3.6 L/h, and after 30 min, the sampling analysis is conducted. The measurement results are shown in FIG. 4. The NH₃ conversion rate gradually increases as the temperature increases, and the NH₃ conversion rate can reach 22% at 380° C.; when the temperature is higher than 380° C., the catalyst activity decreases; and when the temperature is higher than 400° C., the NH₃ conversion rate increases gradually as the temperature increases.

EMBODIMENT 4

In the argon glovebox, Fe₂N of 1.0000 g and KNH₂ of 0.7300 g are accurately taken in a homemade stainless steel ball mill tank. After the ball mill tank is sealed, the sample Fe₂N/KNH₂ (molar ratio is 0.5:2) is prepared by ball-milling Fe₂N and KNH₂ under ball mill condition of 200 rpm in the planetary ball mill (Fischt PM400) for 5 h.

In the argon glovebox, Fe₂N/LiNH₂ (molar ratio is 0.5:2) of 0.0350 g is accurately taken in the fixed bed stainless steel reactor. The sample is heated to a desired temperature in reaction atmosphere (5% NH₃/Ar mixture), the reactant flow rate is controlled between 1.8 L/h and 3.6 L/h, and after 30 min, the sampling analysis is conducted. The measurement results are shown in FIG. 4. The NH₃ conversion rate increases gradually as the temperature increases during the temperature range of 300 to 400° C. The NH₃ conversion rate can reach 16% at 380° C., which is lower than that of the sample Fe₂N/LiNH₂ (molar ratio is 0.5:2).

EMBODIMENT 5

In the argon glovebox, Fe₂N/LiNH₂ (molar ratio is 0.5:3) of 0.0400 g is accurately taken in the fixed bed stainless steel reactor. The sample is heated to the desired reaction temperature in pure ammonia atmosphere, the reactant flow rate is controlled at 2.4 L/h, and after 30 min, the sampling analysis is conducted. The measurement results are shown in FIG. 5. The NH₃ conversion rate increases as the temperature increases during the temperature range of 400 to 475° C., and the NH₃ conversion rate is measured to be 9.2 kgNH₃g_(cat) ⁻¹ h⁻¹ at 470° C.

EMBODIMENT 6

In the argon glovebox, Fe₂N/KNH₂ (molar ratio is 0.5:2) of 0.0400 g is accurately taken in the fixed bed stainless steel reactor. The sample is heated to the desired reaction temperature in pure ammonia atmosphere, the reactant flow rate is controlled at 2.4 L/h, and after 30 min, the sampling analysis is conducted. The measurement results are shown in FIG. 5. The NH₃ conversion rate increases as the temperature increases during the temperature range of 300 to 400° C. The NH₃ conversion rate is measured to be 6.9 kgNH₃g_(cat) ⁻¹ h⁻¹ at 470° C., which is slower than that of the sample Fe₂N/LiNH₂ (molar ratio is 0.5:3).

EMBODIMENT 7

In the argon glovebox, a ball-milled LiH sample of 0.0300 g is accurately taken in a fixed bed stainless steel high-pressure reactor. The sample is heated to 400° C. in N₂/H₂ mixture (volume ratio of N₂ to H₂ is 1:3), the total pressure is 1 atm, the reactant flow rate is 1.8 L/h, and the NH₃ synthesis rate is detected by using the conventional conductivity method. The NH₃ synthesis rate is measured to be 95 umolg_(cat) ⁻¹ h⁻¹ under reaction condition.

EMBODIMENT 8

In the argon glovebox, a Fe/KH sample of 0.0300 g prepared by a ball-milling method is accurately taken in the fixed bed stainless steel high-pressure reactor. The sample is heated to 400° C. in N₂/H₂ mixture (volume ratio of N₂ to H₂ is 1:3), the total pressure is 1 atm, the reactant flow rate is 1.8 L/h, and the NH₃ synthesis rate is detected by using the conventional conductivity method. The NH₃ synthesis rate is measured to be 120 umolg_(cat) ⁻¹ h⁻¹ under reaction condition.

EMBODIMENT 9

In the argon glovebox, a 5 wt % Ru/LiH sample of 0.0560 g homemade by an impregnation method is accurately taken in the fixed bed stainless steel high-pressure reactor. The sample is heated to 400° C. in N₂/H₂ mixture (volume ratio of N₂ to H₂ is 1:3), the total pressure is 10 atm, the reactant flow rate is 2.4 L/h, and the NH₃ synthesis rate is detected by using the conventional conductivity method. The NH₃ synthesis rate is measured to be 75 umolg_(cat) ⁻¹ h⁻¹ under reaction condition.

EMBODIMENT 10

In the argon glovebox, a KNH₂-promoted 5 wt % Ru/LiH sample of 0.1390 g homemade by the impregnation method is accurately taken in the fixed bed stainless steel high-pressure reactor. The sample is heated to 340° C. in N₂/H₂ mixture (volume ratio of N₂ to H₂ is 1:3), the total pressure is 1 atm, the reactant flow rate is 2.4 L/h, and the NH₃ synthesis rate is detected by using the conventional conductivity method. The NH₃ synthesis rate is measured to be 5010 umolg_(cat) ⁻¹ h⁻¹ under reaction condition. 

1. A catalyst for ammonia synthesis and ammonia decomposition, wherein said catalyst is used as a body and/or additive, the body being one or more than two of nitrogen and/or hydrogen-containing compound of a main group element, and the additive comprising one or more selected from support, transition metal nitride or transition metal alloy; the mass ratio of said catalyst body to the additive is in a range from 1000:1 to 1:500.
 2. The catalyst according to claim 1, wherein the formula of the nitrogen and/or hydrogen-containing compound of said main group element is M_(x)N_(y)H_(m(3y-nx)), wherein M is an IA, IIA or IIIA group element, such as one or more selected from Li, Na, K, Rb, Cs, Mg, Ca, Ba and Al, and n (can be 1, 2 and 3) is the valence of M, and m (can be 1 and −1) is the valence of H; when m=1, the formula is M_(x)N_(y)H_(3y-nx), and x=1-3, y=1-3; and when m=−1, the formula is M_(x)N_(y)H_(nx-3y), x=1-4, y=0-1.
 3. The catalyst according to claim 1, wherein said main group element is one selected from Li, Na, K, Cs, Mg, Ca, Ba and Al or a mixture of more than two.
 4. The catalyst according to claim 1, wherein said support is one selected from Li₂O, MgO, CaO, SrO, BaO, Al₂O₃, BN, Si₃N₄, Mg₃N₂, Ca₃N₂, AlN, molecular sieve, carbon material, and Metal-organic Frameworks (MOF) or a combination of more than two.
 5. The catalyst according to claim 1, wherein said transition metal nitride is an IVB, VB, VIB, VIIB or VIIIB group element, such as one nitride of Ti, Zr, V, Nb, Ta, Cr, Mo, W, Mn, Fe, Ru, Co, etc. or a combination of more than two nitrides.
 6. The catalyst according to claim 1, wherein said transition metal alloy is an IVB, VB, VIB, VIIB or VIIIB group element, such as binary or ternary alloy formed by synthesis of two or three of Ti, Zr, V, Nb, Ta, Cr, Mo, W, Mn, Fe, Ru, Co, Rh, Ir, Ni, Pd and Pt, or is the IVB, VB, VIB, VIM or VIIIB group element, such as alloy higher than binary or ternary alloy formed by C and/or B and one or more selected from Ti, Zr, Cr, Mo, W, Mn, Fe, Ru, Co, Rh, Ir, Ni, Pd or Pt.
 7. The catalyst according to claim 1, wherein the mass ratio of said catalyst body to the addictive is in a preferred range from 200:1 to 1:100.
 8. Use of the catalyst according to claim 1, wherein when said catalyst is used for ammonia synthesis, the operating condition is as follows: a sample is heated to 400° C. in a N₂/H₂ mixture (volume ratio of N₂ to H₂ is 1:3), the total pressure is 1 atm to 10 atm, the reactant flow rate is 1.8 to 2.4 L/h, and conventional conductivity method is used for detecting the NH₃ synthesis rate; and when said catalyst is used for ammonia decomposition, the operating condition is as follows: a sample is heated to a certain reaction temperature in Ar or reaction atmosphere (5% NH₃/Ar mixture or pure ammonia), and the on-line analysis is conducted on the product composition by adopting gas chromatography.
 9. The catalyst according to claim 2, wherein said main group element is one selected from Li, Na, K, Cs, Mg, Ca, Ba and Al or a mixture of more than two. 